CC481K Bronze vs. S35000 Stainless Steel
CC481K bronze belongs to the copper alloys classification, while S35000 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is CC481K bronze and the bottom bar is S35000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 4.5 | |
| 2.3 to 14 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 350 | |
| 1300 to 1570 |
| Tensile Strength: Yield (Proof), MPa | 180 | |
| 660 to 1160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 900 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1460 |
| Melting Onset (Solidus), °C | 880 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 470 |
| Thermal Conductivity, W/m-K | 64 | |
| 16 |
| Thermal Expansion, µm/m-K | 18 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 14 |
| Density, g/cm3 | 8.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.7 | |
| 3.2 |
| Embodied Energy, MJ/kg | 60 | |
| 44 |
| Embodied Water, L/kg | 390 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 | |
| 28 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 | |
| 1070 to 3360 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 11 | |
| 46 to 56 |
| Strength to Weight: Bending, points | 13 | |
| 34 to 38 |
| Thermal Diffusivity, mm2/s | 20 | |
| 4.4 |
| Thermal Shock Resistance, points | 13 | |
| 42 to 51 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.070 to 0.11 |
| Chromium (Cr), % | 0 | |
| 16 to 17 |
| Copper (Cu), % | 87 to 89.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 72.7 to 76.9 |
| Lead (Pb), % | 0 to 0.25 | |
| 0 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0.5 to 1.3 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 3.2 |
| Nickel (Ni), % | 0 to 0.1 | |
| 4.0 to 5.0 |
| Nitrogen (N), % | 0 | |
| 0.070 to 0.13 |
| Phosphorus (P), % | 0 to 1.0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.030 |
| Tin (Sn), % | 10 to 11.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |