CC490K Brass vs. C22000 Bronze
Both CC490K brass and C22000 bronze are copper alloys. They have a moderately high 92% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is CC490K brass and the bottom bar is C22000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 15 | |
| 1.9 to 45 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 260 to 520 |
| Tensile Strength: Yield (Proof), MPa | 110 | |
| 69 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 180 |
| Melting Completion (Liquidus), °C | 980 | |
| 1040 |
| Melting Onset (Solidus), °C | 910 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 390 |
| Thermal Conductivity, W/m-K | 72 | |
| 190 |
| Thermal Expansion, µm/m-K | 19 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 16 | |
| 44 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 45 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 29 |
| Density, g/cm3 | 8.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.6 |
| Embodied Energy, MJ/kg | 47 | |
| 42 |
| Embodied Water, L/kg | 340 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 28 | |
| 3.7 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 54 | |
| 21 to 1110 |
| Stiffness to Weight: Axial, points | 6.8 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 7.3 | |
| 8.1 to 17 |
| Strength to Weight: Bending, points | 9.5 | |
| 10 to 17 |
| Thermal Diffusivity, mm2/s | 22 | |
| 56 |
| Thermal Shock Resistance, points | 8.2 | |
| 8.8 to 18 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 81 to 86 | |
| 89 to 91 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.050 |
| Lead (Pb), % | 3.0 to 6.0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 to 2.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 2.0 to 3.5 | |
| 0 |
| Zinc (Zn), % | 7.0 to 9.5 | |
| 8.7 to 11 |
| Residuals, % | 0 | |
| 0 to 0.2 |