CC491K Bronze vs. ASTM A216 Cast Steel

CC491K bronze belongs to the copper alloys classification, while ASTM A216 cast steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CC491K bronze and the bottom bar is ASTM A216 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 13
25 to 27
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 40
72
Tensile Strength: Ultimate (UTS), MPa 260
500 to 570
Tensile Strength: Yield (Proof), MPa 120
230 to 310

Thermal Properties

Latent Heat of Fusion, J/g 190
250
Maximum Temperature: Mechanical, °C 160
400
Melting Completion (Liquidus), °C 980
1450 to 1460
Melting Onset (Solidus), °C 900
1410
Specific Heat Capacity, J/kg-K 370
470
Thermal Conductivity, W/m-K 71
49 to 52
Thermal Expansion, µm/m-K 19
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 15
7.1 to 7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 15
8.2 to 8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.8
Density, g/cm3 8.9
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.4
Embodied Energy, MJ/kg 51
18
Embodied Water, L/kg 350
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 27
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 67
140 to 250
Stiffness to Weight: Axial, points 6.7
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 8.1
18 to 20
Strength to Weight: Bending, points 10
18 to 20
Thermal Diffusivity, mm2/s 22
13 to 14
Thermal Shock Resistance, points 9.3
16 to 18