CC494K Bronze vs. C19700 Copper
Both CC494K bronze and C19700 copper are copper alloys. They have 83% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is CC494K bronze and the bottom bar is C19700 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 120 |
| Elongation at Break, % | 7.6 | |
| 2.4 to 13 |
| Poisson's Ratio | 0.35 | |
| 0.34 |
| Shear Modulus, GPa | 39 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 400 to 530 |
| Tensile Strength: Yield (Proof), MPa | 94 | |
| 330 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 200 |
| Melting Completion (Liquidus), °C | 970 | |
| 1090 |
| Melting Onset (Solidus), °C | 890 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 360 | |
| 390 |
| Thermal Conductivity, W/m-K | 63 | |
| 250 |
| Thermal Expansion, µm/m-K | 19 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 16 | |
| 86 to 88 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 87 to 89 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 30 |
| Density, g/cm3 | 9.1 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 2.6 |
| Embodied Energy, MJ/kg | 50 | |
| 41 |
| Embodied Water, L/kg | 360 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 | |
| 12 to 49 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 43 | |
| 460 to 1160 |
| Stiffness to Weight: Axial, points | 6.4 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 17 | |
| 18 |
| Strength to Weight: Axial, points | 6.5 | |
| 12 to 16 |
| Strength to Weight: Bending, points | 8.8 | |
| 14 to 16 |
| Thermal Diffusivity, mm2/s | 19 | |
| 73 |
| Thermal Shock Resistance, points | 7.8 | |
| 14 to 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 78 to 87 | |
| 97.4 to 99.59 |
| Iron (Fe), % | 0 to 0.25 | |
| 0.3 to 1.2 |
| Lead (Pb), % | 8.0 to 10 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0 | |
| 0.010 to 0.2 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.050 |
| Nickel (Ni), % | 0 to 2.0 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0 to 0.1 | |
| 0.1 to 0.4 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 4.0 to 6.0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 2.0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |