CC496K Bronze vs. AISI 347H Stainless Steel

CC496K bronze belongs to the copper alloys classification, while AISI 347H stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CC496K bronze and the bottom bar is AISI 347H stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 72
170
Elastic (Young's, Tensile) Modulus, GPa 97
200
Elongation at Break, % 8.6
39
Poisson's Ratio 0.35
0.28
Shear Modulus, GPa 36
77
Tensile Strength: Ultimate (UTS), MPa 210
580
Tensile Strength: Yield (Proof), MPa 99
230

Thermal Properties

Latent Heat of Fusion, J/g 170
290
Maximum Temperature: Mechanical, °C 140
940
Melting Completion (Liquidus), °C 900
1430
Melting Onset (Solidus), °C 820
1390
Specific Heat Capacity, J/kg-K 340
480
Thermal Conductivity, W/m-K 52
16
Thermal Expansion, µm/m-K 19
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 11
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 31
19
Density, g/cm3 9.2
7.8
Embodied Carbon, kg CO2/kg material 3.3
3.6
Embodied Energy, MJ/kg 52
52
Embodied Water, L/kg 380
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 15
180
Resilience: Unit (Modulus of Resilience), kJ/m3 50
140
Stiffness to Weight: Axial, points 5.9
14
Stiffness to Weight: Bending, points 17
25
Strength to Weight: Axial, points 6.5
21
Strength to Weight: Bending, points 8.6
20
Thermal Diffusivity, mm2/s 17
4.2
Thermal Shock Resistance, points 8.1
13

Alloy Composition

Aluminum (Al), % 0 to 0.010
0
Antimony (Sb), % 0 to 0.5
0
Carbon (C), % 0
0.040 to 0.1
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 72 to 79.5
0
Iron (Fe), % 0 to 0.25
64.1 to 74
Lead (Pb), % 13 to 17
0
Manganese (Mn), % 0 to 0.2
0 to 2.0
Nickel (Ni), % 0.5 to 2.0
9.0 to 13
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.1
0 to 0.045
Silicon (Si), % 0 to 0.010
0 to 0.75
Sulfur (S), % 0 to 0.1
0 to 0.030
Tin (Sn), % 6.0 to 8.0
0
Zinc (Zn), % 0 to 2.0
0