CC496K Bronze vs. EN 1.4020 Stainless Steel
CC496K bronze belongs to the copper alloys classification, while EN 1.4020 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is CC496K bronze and the bottom bar is EN 1.4020 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 72 | |
| 190 to 340 |
| Elastic (Young's, Tensile) Modulus, GPa | 97 | |
| 200 |
| Elongation at Break, % | 8.6 | |
| 13 to 34 |
| Poisson's Ratio | 0.35 | |
| 0.28 |
| Shear Modulus, GPa | 36 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 770 to 1130 |
| Tensile Strength: Yield (Proof), MPa | 99 | |
| 430 to 950 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 890 |
| Melting Completion (Liquidus), °C | 900 | |
| 1390 |
| Melting Onset (Solidus), °C | 820 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 340 | |
| 480 |
| Thermal Expansion, µm/m-K | 19 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 11 |
| Density, g/cm3 | 9.2 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 2.5 |
| Embodied Energy, MJ/kg | 52 | |
| 37 |
| Embodied Water, L/kg | 380 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 | |
| 140 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 50 | |
| 460 to 2290 |
| Stiffness to Weight: Axial, points | 5.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 17 | |
| 25 |
| Strength to Weight: Axial, points | 6.5 | |
| 28 to 41 |
| Strength to Weight: Bending, points | 8.6 | |
| 25 to 32 |
| Thermal Shock Resistance, points | 8.1 | |
| 16 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 16.5 to 19 |
| Copper (Cu), % | 72 to 79.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 62.8 to 71.8 |
| Lead (Pb), % | 13 to 17 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 11 to 14 |
| Nickel (Ni), % | 0.5 to 2.0 | |
| 0.5 to 2.5 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.45 |
| Phosphorus (P), % | 0 to 0.1 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 to 0.030 |
| Tin (Sn), % | 6.0 to 8.0 | |
| 0 |
| Zinc (Zn), % | 0 to 2.0 | |
| 0 |