CC497K Bronze vs. C90800 Bronze
Both CC497K bronze and C90800 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 78% of their average alloy composition in common.
For each property being compared, the top bar is CC497K bronze and the bottom bar is C90800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 | |
| 90 |
| Elastic (Young's, Tensile) Modulus, GPa | 93 | |
| 110 |
| Elongation at Break, % | 6.7 | |
| 13 |
| Poisson's Ratio | 0.36 | |
| 0.34 |
| Shear Modulus, GPa | 34 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 91 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 160 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 170 |
| Melting Completion (Liquidus), °C | 870 | |
| 990 |
| Melting Onset (Solidus), °C | 800 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 330 | |
| 370 |
| Thermal Conductivity, W/m-K | 53 | |
| 68 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 36 |
| Density, g/cm3 | 9.3 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 3.8 |
| Embodied Energy, MJ/kg | 48 | |
| 62 |
| Embodied Water, L/kg | 370 | |
| 410 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 10 | |
| 35 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 45 | |
| 140 |
| Stiffness to Weight: Axial, points | 5.5 | |
| 6.9 |
| Stiffness to Weight: Bending, points | 16 | |
| 18 |
| Strength to Weight: Axial, points | 5.6 | |
| 11 |
| Strength to Weight: Bending, points | 7.8 | |
| 12 |
| Thermal Diffusivity, mm2/s | 17 | |
| 21 |
| Thermal Shock Resistance, points | 7.2 | |
| 12 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 to 0.75 | |
| 0 to 0.2 |
| Copper (Cu), % | 67.5 to 77.5 | |
| 85.3 to 89 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.15 |
| Lead (Pb), % | 18 to 23 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 |
| Nickel (Ni), % | 0.5 to 2.5 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.1 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 to 0.050 |
| Tin (Sn), % | 4.0 to 6.0 | |
| 11 to 13 |
| Zinc (Zn), % | 0 to 2.0 | |
| 0 to 0.25 |