CC498K Bronze vs. CC753S Brass
Both CC498K bronze and CC753S brass are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 65% of their average alloy composition in common.
For each property being compared, the top bar is CC498K bronze and the bottom bar is CC753S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 78 | |
| 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 14 | |
| 17 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 41 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 340 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 120 |
| Melting Completion (Liquidus), °C | 1000 | |
| 820 |
| Melting Onset (Solidus), °C | 920 | |
| 780 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 390 |
| Thermal Conductivity, W/m-K | 73 | |
| 99 |
| Thermal Expansion, µm/m-K | 18 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 23 |
| Density, g/cm3 | 8.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 2.8 |
| Embodied Energy, MJ/kg | 52 | |
| 47 |
| Embodied Water, L/kg | 360 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 47 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 | |
| 140 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 8.1 | |
| 12 |
| Strength to Weight: Bending, points | 10 | |
| 13 |
| Thermal Diffusivity, mm2/s | 22 | |
| 32 |
| Thermal Shock Resistance, points | 9.3 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0.4 to 0.8 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 to 0.050 |
| Copper (Cu), % | 85 to 90 | |
| 56.8 to 60.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 0.5 to 0.8 |
| Lead (Pb), % | 1.0 to 2.0 | |
| 1.8 to 2.5 |
| Manganese (Mn), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0.5 to 1.2 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.010 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 5.5 to 6.5 | |
| 0 to 0.8 |
| Zinc (Zn), % | 3.0 to 5.0 | |
| 33.1 to 40 |