CC498K Bronze vs. Grade M30C Nickel
CC498K bronze belongs to the copper alloys classification, while grade M30C nickel belongs to the nickel alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is CC498K bronze and the bottom bar is grade M30C nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 160 |
| Elongation at Break, % | 14 | |
| 29 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 41 | |
| 61 |
| Tensile Strength: Ultimate (UTS), MPa | 260 | |
| 510 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 900 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1290 |
| Melting Onset (Solidus), °C | 920 | |
| 1240 |
| Specific Heat Capacity, J/kg-K | 370 | |
| 430 |
| Thermal Conductivity, W/m-K | 73 | |
| 22 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 32 | |
| 60 |
| Density, g/cm3 | 8.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 9.5 |
| Embodied Energy, MJ/kg | 52 | |
| 140 |
| Embodied Water, L/kg | 360 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 72 | |
| 200 |
| Stiffness to Weight: Axial, points | 6.9 | |
| 10 |
| Stiffness to Weight: Bending, points | 18 | |
| 21 |
| Strength to Weight: Axial, points | 8.1 | |
| 16 |
| Strength to Weight: Bending, points | 10 | |
| 16 |
| Thermal Diffusivity, mm2/s | 22 | |
| 5.7 |
| Thermal Shock Resistance, points | 9.3 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.25 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 85 to 90 | |
| 26 to 33 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 3.5 |
| Lead (Pb), % | 1.0 to 2.0 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 to 1.0 | |
| 56.6 to 72 |
| Niobium (Nb), % | 0 | |
| 1.0 to 3.0 |
| Phosphorus (P), % | 0 to 0.050 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.010 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 to 0.1 | |
| 0 to 0.030 |
| Tin (Sn), % | 5.5 to 6.5 | |
| 0 |
| Zinc (Zn), % | 3.0 to 5.0 | |
| 0 |