CC751S Brass vs. ASTM B780 Alloy

CC751S brass belongs to the copper alloys classification, while ASTM B780 alloy belongs to the otherwise unclassified metals. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 16 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is CC751S brass and the bottom bar is ASTM B780 alloy.

EN CC751S (CuZn33Pb2Si-C) Leaded Brass ASTM B780 Silver-Copper-Nickel Electrical Contact Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		110
Elastic (Young's, Tensile) Modulus, GPa		83

Elongation at Break, %		5.6
Elongation at Break, %		1.1 to 9.1

Poisson's Ratio		0.31
Poisson's Ratio		0.36

Shear Modulus, GPa		40
Shear Modulus, GPa		30

Tensile Strength: Ultimate (UTS), MPa		450
Tensile Strength: Ultimate (UTS), MPa		330 to 590

Thermal Properties

Latent Heat of Fusion, J/g		190
Latent Heat of Fusion, J/g		140

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		270

Thermal Expansion, µm/m-K		20
Thermal Expansion, µm/m-K		18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		25
Electrical Conductivity: Equal Volume, % IACS		70 to 76

Electrical Conductivity: Equal Weight (Specific), % IACS		28
Electrical Conductivity: Equal Weight (Specific), % IACS		62 to 68

Otherwise Unclassified Properties

Density, g/cm³		8.1
Density, g/cm³		10

Common Calculations

Stiffness to Weight: Axial, points		7.2
Stiffness to Weight: Axial, points		4.5

Stiffness to Weight: Bending, points		19
Stiffness to Weight: Bending, points		14

Strength to Weight: Axial, points		15
Strength to Weight: Axial, points		9.1 to 16

Strength to Weight: Bending, points		16
Strength to Weight: Bending, points		11 to 15

Thermal Shock Resistance, points		15
Thermal Shock Resistance, points		16 to 29

Alloy Composition

Aluminum (Al), %		0 to 0.1
Aluminum (Al), %		0

Antimony (Sb), %		0 to 0.5
Antimony (Sb), %		0

Cadmium (Cd), %		0
Cadmium (Cd), %		0 to 0.050

Copper (Cu), %		62.7 to 66
Copper (Cu), %		23.5 to 25.7

Iron (Fe), %		0.25 to 0.5
Iron (Fe), %		0 to 0.050

Lead (Pb), %		0.8 to 2.2
Lead (Pb), %		0 to 0.030

Manganese (Mn), %		0 to 0.15
Manganese (Mn), %		0

Nickel (Ni), %		0 to 0.8
Nickel (Ni), %		0.35 to 0.65

Silicon (Si), %		0.65 to 1.1
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		74 to 76

Tin (Sn), %		0 to 0.8
Tin (Sn), %		0

Zinc (Zn), %		27.9 to 35.6
Zinc (Zn), %		0 to 0.060