CC751S Brass vs. C82600 Copper
Both CC751S brass and C82600 copper are copper alloys. They have 65% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is CC751S brass and the bottom bar is C82600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 5.6 | |
| 1.0 to 20 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 40 | |
| 46 |
| Tensile Strength: Ultimate (UTS), MPa | 450 | |
| 570 to 1140 |
| Tensile Strength: Yield (Proof), MPa | 320 | |
| 320 to 1070 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 300 |
| Melting Completion (Liquidus), °C | 850 | |
| 950 |
| Melting Onset (Solidus), °C | 810 | |
| 860 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 110 | |
| 130 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 28 | |
| 20 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 11 |
| Embodied Energy, MJ/kg | 46 | |
| 180 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 23 | |
| 11 to 97 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 | |
| 430 to 4690 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 15 | |
| 18 to 36 |
| Strength to Weight: Bending, points | 16 | |
| 17 to 28 |
| Thermal Diffusivity, mm2/s | 35 | |
| 37 |
| Thermal Shock Resistance, points | 15 | |
| 19 to 39 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 0 to 0.1 | |
| 0 to 0.15 |
| Antimony (Sb), % | 0 to 0.5 | |
| 0 |
| Beryllium (Be), % | 0 | |
| 2.3 to 2.6 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Cobalt (Co), % | 0 | |
| 0.35 to 0.65 |
| Copper (Cu), % | 62.7 to 66 | |
| 94.9 to 97.2 |
| Iron (Fe), % | 0.25 to 0.5 | |
| 0 to 0.25 |
| Lead (Pb), % | 0.8 to 2.2 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.15 | |
| 0 |
| Nickel (Ni), % | 0 to 0.8 | |
| 0 to 0.2 |
| Silicon (Si), % | 0.65 to 1.1 | |
| 0.2 to 0.35 |
| Tin (Sn), % | 0 to 0.8 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 | |
| 0 to 0.12 |
| Zinc (Zn), % | 27.9 to 35.6 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.5 |