CC763S Brass vs. C21000 Brass
Both CC763S brass and C21000 brass are copper alloys. They have 67% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is CC763S brass and the bottom bar is C21000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 7.3 | |
| 2.9 to 50 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 41 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 240 to 450 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 69 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 200 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 190 |
| Melting Completion (Liquidus), °C | 870 | |
| 1070 |
| Melting Onset (Solidus), °C | 830 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 56 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 32 | |
| 57 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 30 |
| Density, g/cm3 | 8.0 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.6 |
| Embodied Energy, MJ/kg | 49 | |
| 42 |
| Embodied Water, L/kg | 330 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 | |
| 13 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 340 | |
| 21 to 830 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 17 | |
| 7.4 to 14 |
| Strength to Weight: Bending, points | 17 | |
| 9.6 to 15 |
| Thermal Shock Resistance, points | 16 | |
| 8.1 to 15 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Aluminum (Al), % | 1.0 to 2.5 | |
| 0 |
| Antimony (Sb), % | 0 to 0.080 | |
| 0 |
| Copper (Cu), % | 56.5 to 67 | |
| 94 to 96 |
| Iron (Fe), % | 0.5 to 2.0 | |
| 0 to 0.050 |
| Lead (Pb), % | 0 to 1.5 | |
| 0 to 0.030 |
| Manganese (Mn), % | 1.0 to 3.5 | |
| 0 |
| Nickel (Ni), % | 0 to 2.5 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Tin (Sn), % | 0 to 1.0 | |
| 0 |
| Zinc (Zn), % | 18.9 to 41 | |
| 3.7 to 6.0 |
| Residuals, % | 0 | |
| 0 to 0.2 |