CC765S Brass vs. CC381H Copper-nickel

Both CC765S brass and CC381H copper-nickel are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 63% of their average alloy composition in common.

For each property being compared, the top bar is CC765S brass and the bottom bar is CC381H copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
91
Elastic (Young's, Tensile) Modulus, GPa 110
140
Elongation at Break, % 21
20
Poisson's Ratio 0.31
0.33
Shear Modulus, GPa 42
52
Tensile Strength: Ultimate (UTS), MPa 540
380
Tensile Strength: Yield (Proof), MPa 220
140

Thermal Properties

Latent Heat of Fusion, J/g 180
240
Maximum Temperature: Mechanical, °C 140
260
Melting Completion (Liquidus), °C 860
1180
Melting Onset (Solidus), °C 820
1120
Specific Heat Capacity, J/kg-K 400
410
Thermal Conductivity, W/m-K 91
30
Thermal Expansion, µm/m-K 20
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30
6.8
Electrical Conductivity: Equal Weight (Specific), % IACS 34
6.9

Otherwise Unclassified Properties

Base Metal Price, % relative 24
40
Density, g/cm3 8.0
8.9
Embodied Carbon, kg CO2/kg material 3.0
5.0
Embodied Energy, MJ/kg 51
73
Embodied Water, L/kg 330
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
60
Resilience: Unit (Modulus of Resilience), kJ/m3 220
68
Stiffness to Weight: Axial, points 7.6
8.6
Stiffness to Weight: Bending, points 20
19
Strength to Weight: Axial, points 19
12
Strength to Weight: Bending, points 18
13
Thermal Diffusivity, mm2/s 28
8.4
Thermal Shock Resistance, points 17
13

Alloy Composition

Aluminum (Al), % 0.5 to 2.5
0 to 0.010
Antimony (Sb), % 0 to 0.080
0
Carbon (C), % 0
0 to 0.030
Copper (Cu), % 51 to 65
64.5 to 69.9
Iron (Fe), % 0.5 to 2.0
0.5 to 1.5
Lead (Pb), % 0 to 0.5
0 to 0.030
Manganese (Mn), % 0.3 to 3.0
0.6 to 1.2
Nickel (Ni), % 0 to 6.0
29 to 31
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 0.1
0 to 0.1
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0 to 1.0
0
Zinc (Zn), % 19.8 to 47.7
0 to 0.5