CC767S Brass vs. 88-silver 12-tin-oxide
CC767S brass belongs to the copper alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 5 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is CC767S brass and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 84 to 86 |
| Elongation at Break, % | 34 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 24 to 70 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 150 | |
| 110 to 260 |