CR008A Copper vs. 1200 Aluminum

CR008A copper belongs to the copper alloys classification, while 1200 aluminum belongs to the aluminum alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is CR008A copper and the bottom bar is 1200 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
69
Elongation at Break, % 15
1.1 to 28
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 43
26
Tensile Strength: Ultimate (UTS), MPa 220
85 to 180
Tensile Strength: Yield (Proof), MPa 130
28 to 160

Thermal Properties

Latent Heat of Fusion, J/g 210
400
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 1090
660
Melting Onset (Solidus), °C 1040
650
Specific Heat Capacity, J/kg-K 390
900
Thermal Conductivity, W/m-K 380
230
Thermal Expansion, µm/m-K 17
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
58
Electrical Conductivity: Equal Weight (Specific), % IACS 100
190

Otherwise Unclassified Properties

Base Metal Price, % relative 31
9.0
Density, g/cm3 9.0
2.7
Embodied Carbon, kg CO2/kg material 2.6
8.2
Embodied Energy, MJ/kg 41
150
Embodied Water, L/kg 320
1190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
2.0 to 19
Resilience: Unit (Modulus of Resilience), kJ/m3 76
5.7 to 180
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
50
Strength to Weight: Axial, points 6.8
8.7 to 19
Strength to Weight: Bending, points 9.0
16 to 26
Thermal Diffusivity, mm2/s 110
92
Thermal Shock Resistance, points 7.8
3.8 to 8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
99 to 100
Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.95 to 100
0 to 0.050
Iron (Fe), % 0
0 to 1.0
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0
0 to 0.050
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.050
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15