CR009A Copper vs. AWS BNi-9

CR009A copper belongs to the copper alloys classification, while AWS BNi-9 belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is CR009A copper and the bottom bar is AWS BNi-9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Poisson's Ratio 0.34
0.3
Shear Modulus, GPa 43
72
Tensile Strength: Ultimate (UTS), MPa 230
580

Thermal Properties

Latent Heat of Fusion, J/g 210
300
Melting Completion (Liquidus), °C 1090
1060
Melting Onset (Solidus), °C 1040
1060
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Base Metal Price, % relative 31
60
Density, g/cm3 9.0
8.4
Embodied Carbon, kg CO2/kg material 2.6
9.3
Embodied Energy, MJ/kg 41
130
Embodied Water, L/kg 310
260

Common Calculations

Stiffness to Weight: Axial, points 7.2
12
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 7.1
19
Strength to Weight: Bending, points 9.3
18
Thermal Shock Resistance, points 8.1
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Boron (B), % 0
3.3 to 4.0
Cadmium (Cd), % 0 to 0.00010
0
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
13.5 to 16.5
Cobalt (Co), % 0
0 to 0.1
Copper (Cu), % 99.99 to 100
0
Iron (Fe), % 0 to 0.0010
0 to 1.5
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0
Nickel (Ni), % 0 to 0.0010
77.1 to 83.3
Phosphorus (P), % 0 to 0.0030
0 to 0.020
Selenium (Se), % 0 to 0.00020
0 to 0.0050
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.020
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Titanium (Ti), % 0
0 to 0.050
Zinc (Zn), % 0 to 0.00010
0
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5