CR009A Copper vs. CC483K Bronze

Both CR009A copper and CC483K bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 87% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is CR009A copper and the bottom bar is CC483K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 15
6.4
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
40
Tensile Strength: Ultimate (UTS), MPa 230
310
Tensile Strength: Yield (Proof), MPa 140
170

Thermal Properties

Latent Heat of Fusion, J/g 210
190
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 1090
990
Melting Onset (Solidus), °C 1040
870
Specific Heat Capacity, J/kg-K 390
370
Thermal Conductivity, W/m-K 380
68
Thermal Expansion, µm/m-K 17
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
10
Electrical Conductivity: Equal Weight (Specific), % IACS 100
10

Otherwise Unclassified Properties

Base Metal Price, % relative 31
36
Density, g/cm3 9.0
8.7
Embodied Carbon, kg CO2/kg material 2.6
3.8
Embodied Energy, MJ/kg 41
62
Embodied Water, L/kg 310
400

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
17
Resilience: Unit (Modulus of Resilience), kJ/m3 83
130
Stiffness to Weight: Axial, points 7.2
6.9
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 7.1
9.9
Strength to Weight: Bending, points 9.3
12
Thermal Diffusivity, mm2/s 110
21
Thermal Shock Resistance, points 8.1
11

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0 to 0.00040
0 to 0.15
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Copper (Cu), % 99.99 to 100
85 to 89
Iron (Fe), % 0 to 0.0010
0 to 0.2
Lead (Pb), % 0 to 0.00050
0 to 0.7
Manganese (Mn), % 0 to 0.00050
0 to 0.2
Nickel (Ni), % 0 to 0.0010
0 to 2.0
Phosphorus (P), % 0 to 0.0030
0 to 0.6
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.010
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.050
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
10.5 to 13
Zinc (Zn), % 0 to 0.00010
0 to 0.5