CR009A Copper vs. C27400 Brass

Both CR009A copper and C27400 brass are copper alloys. They have 63% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CR009A copper and the bottom bar is C27400 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Poisson's Ratio 0.34
0.31
Shear Modulus, GPa 43
40
Tensile Strength: Ultimate (UTS), MPa 230
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 210
170
Maximum Temperature: Mechanical, °C 200
120
Melting Completion (Liquidus), °C 1090
920
Melting Onset (Solidus), °C 1040
870
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 380
120
Thermal Expansion, µm/m-K 17
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
28
Electrical Conductivity: Equal Weight (Specific), % IACS 100
31

Otherwise Unclassified Properties

Base Metal Price, % relative 31
23
Density, g/cm3 9.0
8.0
Embodied Carbon, kg CO2/kg material 2.6
2.7
Embodied Energy, MJ/kg 41
45
Embodied Water, L/kg 310
320

Common Calculations

Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
20
Strength to Weight: Axial, points 7.1
13 to 23
Strength to Weight: Bending, points 9.3
14 to 21
Thermal Diffusivity, mm2/s 110
37
Thermal Shock Resistance, points 8.1
12 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Copper (Cu), % 99.99 to 100
61 to 64
Iron (Fe), % 0 to 0.0010
0 to 0.1
Lead (Pb), % 0 to 0.00050
0 to 0.050
Manganese (Mn), % 0 to 0.00050
0
Nickel (Ni), % 0 to 0.0010
0
Phosphorus (P), % 0 to 0.0030
0
Selenium (Se), % 0 to 0.00020
0
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Zinc (Zn), % 0 to 0.00010
35.6 to 39
Residuals, % 0
0 to 0.3