CR009A Copper vs. C97300 Nickel Silver

Both CR009A copper and C97300 nickel silver are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 56% of their average alloy composition in common.

For each property being compared, the top bar is CR009A copper and the bottom bar is C97300 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 15
9.0
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 43
40
Tensile Strength: Ultimate (UTS), MPa 230
230
Tensile Strength: Yield (Proof), MPa 140
110

Thermal Properties

Latent Heat of Fusion, J/g 210
180
Maximum Temperature: Mechanical, °C 200
150
Melting Completion (Liquidus), °C 1090
1040
Melting Onset (Solidus), °C 1040
1010
Specific Heat Capacity, J/kg-K 390
370
Thermal Conductivity, W/m-K 380
29
Thermal Expansion, µm/m-K 17
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
6.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
30
Density, g/cm3 9.0
8.6
Embodied Carbon, kg CO2/kg material 2.6
3.7
Embodied Energy, MJ/kg 41
59
Embodied Water, L/kg 310
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
18
Resilience: Unit (Modulus of Resilience), kJ/m3 83
59
Stiffness to Weight: Axial, points 7.2
7.0
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 7.1
7.6
Strength to Weight: Bending, points 9.3
9.8
Thermal Diffusivity, mm2/s 110
9.3
Thermal Shock Resistance, points 8.1
8.0

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0 to 0.00040
0 to 0.35
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Copper (Cu), % 99.99 to 100
53 to 58
Iron (Fe), % 0 to 0.0010
0 to 1.5
Lead (Pb), % 0 to 0.00050
8.0 to 11
Manganese (Mn), % 0 to 0.00050
0
Nickel (Ni), % 0 to 0.0010
11 to 14
Phosphorus (P), % 0 to 0.0030
0 to 0.050
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.15
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.080
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
1.5 to 3.0
Zinc (Zn), % 0 to 0.00010
17 to 25
Residuals, % 0
0 to 1.0