CR009A Copper vs. N06200 Nickel

CR009A copper belongs to the copper alloys classification, while N06200 nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CR009A copper and the bottom bar is N06200 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
220
Elongation at Break, % 15
51
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
84
Tensile Strength: Ultimate (UTS), MPa 230
780
Tensile Strength: Yield (Proof), MPa 140
320

Thermal Properties

Latent Heat of Fusion, J/g 210
330
Maximum Temperature: Mechanical, °C 200
990
Melting Completion (Liquidus), °C 1090
1500
Melting Onset (Solidus), °C 1040
1450
Specific Heat Capacity, J/kg-K 390
430
Thermal Conductivity, W/m-K 380
9.1
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 100
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
65
Density, g/cm3 9.0
8.7
Embodied Carbon, kg CO2/kg material 2.6
12
Embodied Energy, MJ/kg 41
160
Embodied Water, L/kg 310
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
320
Resilience: Unit (Modulus of Resilience), kJ/m3 83
240
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 7.1
25
Strength to Weight: Bending, points 9.3
22
Thermal Diffusivity, mm2/s 110
2.4
Thermal Shock Resistance, points 8.1
21

Alloy Composition

Aluminum (Al), % 0
0 to 0.5
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0
22 to 24
Cobalt (Co), % 0
0 to 2.0
Copper (Cu), % 99.99 to 100
1.3 to 1.9
Iron (Fe), % 0 to 0.0010
0 to 3.0
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0 to 0.010
Molybdenum (Mo), % 0
15 to 17
Nickel (Ni), % 0 to 0.0010
51 to 61.7
Phosphorus (P), % 0 to 0.0030
0 to 0.025
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.080
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.010
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Zinc (Zn), % 0 to 0.00010
0