CR011A Copper vs. ASTM A387 Grade 5 Steel

CR011A copper belongs to the copper alloys classification, while ASTM A387 grade 5 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is CR011A copper and the bottom bar is ASTM A387 grade 5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
20 to 21
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
74
Tensile Strength: Ultimate (UTS), MPa 220
500 to 600
Tensile Strength: Yield (Proof), MPa 130
230 to 350

Thermal Properties

Latent Heat of Fusion, J/g 210
260
Maximum Temperature: Mechanical, °C 200
510
Melting Completion (Liquidus), °C 1090
1460
Melting Onset (Solidus), °C 1040
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 390
40
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 32
4.3
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.7
Embodied Energy, MJ/kg 42
23
Embodied Water, L/kg 340
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
83 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 76
140 to 320
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 6.8
18 to 21
Strength to Weight: Bending, points 9.0
18 to 20
Thermal Diffusivity, mm2/s 110
11
Thermal Shock Resistance, points 7.8
14 to 17

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
4.0 to 6.0
Copper (Cu), % 99.88 to 99.97
0
Iron (Fe), % 0
92.1 to 95.3
Manganese (Mn), % 0
0.3 to 0.6
Molybdenum (Mo), % 0
0.45 to 0.65
Oxygen (O), % 0 to 0.040
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 0.030 to 0.050
0
Sulfur (S), % 0
0 to 0.025