CR011A Copper vs. AWS E307

CR011A copper belongs to the copper alloys classification, while AWS E307 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR011A copper and the bottom bar is AWS E307.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 15
34
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
78
Tensile Strength: Ultimate (UTS), MPa 220
660

Thermal Properties

Latent Heat of Fusion, J/g 210
290
Melting Completion (Liquidus), °C 1090
1420
Melting Onset (Solidus), °C 1040
1370
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 390
15
Thermal Expansion, µm/m-K 17
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 100
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 32
17
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
3.5
Embodied Energy, MJ/kg 42
49
Embodied Water, L/kg 340
160

Common Calculations

Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 6.8
24
Strength to Weight: Bending, points 9.0
22
Thermal Diffusivity, mm2/s 110
4.1
Thermal Shock Resistance, points 7.8
17

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0.040 to 0.14
Chromium (Cr), % 0
18 to 21.5
Copper (Cu), % 99.88 to 99.97
0 to 0.75
Iron (Fe), % 0
59.6 to 69.2
Manganese (Mn), % 0
3.3 to 4.8
Molybdenum (Mo), % 0
0.5 to 1.5
Nickel (Ni), % 0
9.0 to 10.7
Oxygen (O), % 0 to 0.040
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0.030 to 0.050
0
Sulfur (S), % 0
0 to 0.030