CR011A Copper vs. EN 1.4922 Stainless Steel

CR011A copper belongs to the copper alloys classification, while EN 1.4922 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR011A copper and the bottom bar is EN 1.4922 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
16
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
76
Tensile Strength: Ultimate (UTS), MPa 220
770
Tensile Strength: Yield (Proof), MPa 130
550

Thermal Properties

Latent Heat of Fusion, J/g 210
270
Maximum Temperature: Mechanical, °C 200
720
Melting Completion (Liquidus), °C 1090
1460
Melting Onset (Solidus), °C 1040
1410
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 390
24
Thermal Expansion, µm/m-K 17
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 100
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 32
7.5
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
2.8
Embodied Energy, MJ/kg 42
40
Embodied Water, L/kg 340
100

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
110
Resilience: Unit (Modulus of Resilience), kJ/m3 76
770
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 6.8
27
Strength to Weight: Bending, points 9.0
24
Thermal Diffusivity, mm2/s 110
6.5
Thermal Shock Resistance, points 7.8
27

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0.17 to 0.23
Chromium (Cr), % 0
10 to 12.5
Copper (Cu), % 99.88 to 99.97
0
Iron (Fe), % 0
83.5 to 88.2
Manganese (Mn), % 0
0.3 to 1.0
Molybdenum (Mo), % 0
0.8 to 1.2
Nickel (Ni), % 0
0.3 to 0.8
Oxygen (O), % 0 to 0.040
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0
0 to 0.4
Silver (Ag), % 0.030 to 0.050
0
Sulfur (S), % 0
0 to 0.015
Vanadium (V), % 0
0.2 to 0.35