CR016A Copper vs. AWS ENiCrCoMo-1

CR016A copper belongs to the copper alloys classification, while AWS ENiCrCoMo-1 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is CR016A copper and the bottom bar is AWS ENiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
210
Elongation at Break, % 15
28
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
82
Tensile Strength: Ultimate (UTS), MPa 230
710

Thermal Properties

Latent Heat of Fusion, J/g 210
330
Melting Completion (Liquidus), °C 1090
1430
Melting Onset (Solidus), °C 1040
1380
Specific Heat Capacity, J/kg-K 390
440
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 35
75
Density, g/cm3 9.0
8.5
Embodied Carbon, kg CO2/kg material 2.7
11
Embodied Energy, MJ/kg 42
140
Embodied Water, L/kg 390
340

Common Calculations

Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 7.1
23
Strength to Weight: Bending, points 9.3
21
Thermal Shock Resistance, points 8.1
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
21 to 26
Cobalt (Co), % 0
9.0 to 15
Copper (Cu), % 99.843 to 99.919
0 to 0.5
Iron (Fe), % 0
0 to 5.0
Manganese (Mn), % 0
0.3 to 2.5
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0
38.6 to 61.7
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0.0010 to 0.0070
0 to 0.030
Silicon (Si), % 0
0 to 0.75
Silver (Ag), % 0.080 to 0.12
0
Sulfur (S), % 0
0 to 0.015
Residuals, % 0
0 to 0.5