CR016A Copper vs. EN 2.4878 Nickel

CR016A copper belongs to the copper alloys classification, while EN 2.4878 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is CR016A copper and the bottom bar is EN 2.4878 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 15
13 to 17
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
78
Tensile Strength: Ultimate (UTS), MPa 230
1210 to 1250
Tensile Strength: Yield (Proof), MPa 140
740 to 780

Thermal Properties

Latent Heat of Fusion, J/g 210
330
Maximum Temperature: Mechanical, °C 200
1030
Melting Completion (Liquidus), °C 1090
1370
Melting Onset (Solidus), °C 1040
1320
Specific Heat Capacity, J/kg-K 390
460
Thermal Conductivity, W/m-K 390
11
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Base Metal Price, % relative 35
80
Density, g/cm3 9.0
8.3
Embodied Carbon, kg CO2/kg material 2.7
10
Embodied Energy, MJ/kg 42
150
Embodied Water, L/kg 390
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
150 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 83
1370 to 1540
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
41 to 42
Strength to Weight: Bending, points 9.3
31
Thermal Diffusivity, mm2/s 110
2.8
Thermal Shock Resistance, points 8.1
37 to 39

Alloy Composition

Aluminum (Al), % 0
1.2 to 1.6
Bismuth (Bi), % 0 to 0.00050
0
Boron (B), % 0
0.010 to 0.015
Carbon (C), % 0
0.030 to 0.070
Chromium (Cr), % 0
23 to 25
Cobalt (Co), % 0
19 to 21
Copper (Cu), % 99.843 to 99.919
0 to 0.2
Iron (Fe), % 0
0 to 1.0
Manganese (Mn), % 0
0 to 0.5
Molybdenum (Mo), % 0
1.0 to 2.0
Nickel (Ni), % 0
43.6 to 52.2
Niobium (Nb), % 0
0.7 to 1.2
Phosphorus (P), % 0.0010 to 0.0070
0 to 0.010
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 0.080 to 0.12
0
Sulfur (S), % 0
0 to 0.0070
Tantalum (Ta), % 0
0 to 0.050
Titanium (Ti), % 0
2.8 to 3.2
Zirconium (Zr), % 0
0.030 to 0.070