CR016A Copper vs. Grade CU5MCuC Nickel

CR016A copper belongs to the copper alloys classification, while grade CU5MCuC nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is CR016A copper and the bottom bar is grade CU5MCuC nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 15
22
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
77
Tensile Strength: Ultimate (UTS), MPa 230
580
Tensile Strength: Yield (Proof), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 210
310
Maximum Temperature: Mechanical, °C 200
980
Melting Completion (Liquidus), °C 1090
1420
Melting Onset (Solidus), °C 1040
1370
Specific Heat Capacity, J/kg-K 390
460
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 35
45
Density, g/cm3 9.0
8.2
Embodied Carbon, kg CO2/kg material 2.7
7.7
Embodied Energy, MJ/kg 42
110
Embodied Water, L/kg 390
230

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
110
Resilience: Unit (Modulus of Resilience), kJ/m3 83
190
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
20
Strength to Weight: Bending, points 9.3
19
Thermal Shock Resistance, points 8.1
16

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
19.5 to 23.5
Copper (Cu), % 99.843 to 99.919
1.5 to 3.5
Iron (Fe), % 0
22.2 to 37.9
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 0
38 to 44
Niobium (Nb), % 0
0.6 to 1.2
Phosphorus (P), % 0.0010 to 0.0070
0 to 0.030
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0.080 to 0.12
0
Sulfur (S), % 0
0 to 0.030