CR016A Copper vs. C10100 Copper

Both CR016A copper and C10100 copper are copper alloys. Their average alloy composition is basically identical. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CR016A copper and the bottom bar is C10100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 15
1.5 to 50
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
43
Tensile Strength: Ultimate (UTS), MPa 230
220 to 410
Tensile Strength: Yield (Proof), MPa 140
69 to 400

Thermal Properties

Latent Heat of Fusion, J/g 210
210
Maximum Temperature: Mechanical, °C 200
200
Melting Completion (Liquidus), °C 1090
1080
Melting Onset (Solidus), °C 1040
1080
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 390
390
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 98
100
Electrical Conductivity: Equal Weight (Specific), % IACS 99
100

Otherwise Unclassified Properties

Base Metal Price, % relative 35
31
Density, g/cm3 9.0
9.0
Embodied Carbon, kg CO2/kg material 2.7
2.6
Embodied Energy, MJ/kg 42
41
Embodied Water, L/kg 390
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
6.1 to 85
Resilience: Unit (Modulus of Resilience), kJ/m3 83
21 to 690
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 7.1
6.8 to 13
Strength to Weight: Bending, points 9.3
9.0 to 14
Thermal Diffusivity, mm2/s 110
110
Thermal Shock Resistance, points 8.1
7.8 to 15

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.843 to 99.919
99.99 to 100
Lead (Pb), % 0
0 to 0.0010
Oxygen (O), % 0
0 to 0.00050
Phosphorus (P), % 0.0010 to 0.0070
0 to 0.00030
Silver (Ag), % 0.080 to 0.12
0
Zinc (Zn), % 0
0 to 0.00010