CR016A Copper vs. C69710 Brass

Both CR016A copper and C69710 brass are copper alloys. They have 78% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is CR016A copper and the bottom bar is C69710 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 15
25
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 43
41
Tensile Strength: Ultimate (UTS), MPa 230
470
Tensile Strength: Yield (Proof), MPa 140
230

Thermal Properties

Latent Heat of Fusion, J/g 210
240
Maximum Temperature: Mechanical, °C 200
160
Melting Completion (Liquidus), °C 1090
930
Melting Onset (Solidus), °C 1040
880
Specific Heat Capacity, J/kg-K 390
400
Thermal Conductivity, W/m-K 390
40
Thermal Expansion, µm/m-K 17
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 98
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 99
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 35
26
Density, g/cm3 9.0
8.3
Embodied Carbon, kg CO2/kg material 2.7
2.7
Embodied Energy, MJ/kg 42
44
Embodied Water, L/kg 390
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
99
Resilience: Unit (Modulus of Resilience), kJ/m3 83
250
Stiffness to Weight: Axial, points 7.2
7.3
Stiffness to Weight: Bending, points 18
19
Strength to Weight: Axial, points 7.1
16
Strength to Weight: Bending, points 9.3
16
Thermal Diffusivity, mm2/s 110
12
Thermal Shock Resistance, points 8.1
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Arsenic (As), % 0
0.030 to 0.060
Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.843 to 99.919
75 to 80
Iron (Fe), % 0
0 to 0.2
Lead (Pb), % 0
0.5 to 1.5
Manganese (Mn), % 0
0 to 0.4
Phosphorus (P), % 0.0010 to 0.0070
0
Silicon (Si), % 0
2.5 to 3.5
Silver (Ag), % 0.080 to 0.12
0
Zinc (Zn), % 0
13.8 to 22
Residuals, % 0
0 to 0.5