CR016A Copper vs. N08026 Nickel

CR016A copper belongs to the copper alloys classification, while N08026 nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CR016A copper and the bottom bar is N08026 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 15
34
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
80
Tensile Strength: Ultimate (UTS), MPa 230
620
Tensile Strength: Yield (Proof), MPa 140
270

Thermal Properties

Latent Heat of Fusion, J/g 210
310
Maximum Temperature: Mechanical, °C 200
990
Melting Completion (Liquidus), °C 1090
1430
Melting Onset (Solidus), °C 1040
1380
Specific Heat Capacity, J/kg-K 390
460
Thermal Conductivity, W/m-K 390
12
Thermal Expansion, µm/m-K 17
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 98
1.6
Electrical Conductivity: Equal Weight (Specific), % IACS 99
1.7

Otherwise Unclassified Properties

Base Metal Price, % relative 35
41
Density, g/cm3 9.0
8.2
Embodied Carbon, kg CO2/kg material 2.7
7.2
Embodied Energy, MJ/kg 42
98
Embodied Water, L/kg 390
240

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
170
Resilience: Unit (Modulus of Resilience), kJ/m3 83
180
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
21
Strength to Weight: Bending, points 9.3
20
Thermal Diffusivity, mm2/s 110
3.2
Thermal Shock Resistance, points 8.1
15

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
22 to 26
Copper (Cu), % 99.843 to 99.919
2.0 to 4.0
Iron (Fe), % 0
24.4 to 37.9
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
5.0 to 6.7
Nickel (Ni), % 0
33 to 37.2
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0.0010 to 0.0070
0 to 0.030
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 0.080 to 0.12
0
Sulfur (S), % 0
0 to 0.030