CR016A Copper vs. N08120 Nickel
CR016A copper belongs to the copper alloys classification, while N08120 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is CR016A copper and the bottom bar is N08120 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 15 | |
| 34 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 43 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 700 |
| Tensile Strength: Yield (Proof), MPa | 140 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 210 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1420 |
| Melting Onset (Solidus), °C | 1040 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 470 |
| Thermal Conductivity, W/m-K | 390 | |
| 11 |
| Thermal Expansion, µm/m-K | 17 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 35 | |
| 45 |
| Density, g/cm3 | 9.0 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 7.2 |
| Embodied Energy, MJ/kg | 42 | |
| 100 |
| Embodied Water, L/kg | 390 | |
| 240 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 83 | |
| 240 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 7.1 | |
| 24 |
| Strength to Weight: Bending, points | 9.3 | |
| 21 |
| Thermal Diffusivity, mm2/s | 110 | |
| 3.0 |
| Thermal Shock Resistance, points | 8.1 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.4 |
| Bismuth (Bi), % | 0 to 0.00050 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.010 |
| Carbon (C), % | 0 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 0 | |
| 23 to 27 |
| Cobalt (Co), % | 0 | |
| 0 to 3.0 |
| Copper (Cu), % | 99.843 to 99.919 | |
| 0 to 0.5 |
| Iron (Fe), % | 0 | |
| 21 to 41.4 |
| Manganese (Mn), % | 0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 2.5 |
| Nickel (Ni), % | 0 | |
| 35 to 39 |
| Niobium (Nb), % | 0 | |
| 0.4 to 0.9 |
| Nitrogen (N), % | 0 | |
| 0.15 to 0.3 |
| Phosphorus (P), % | 0.0010 to 0.0070 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 0.080 to 0.12 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Tungsten (W), % | 0 | |
| 0 to 2.5 |