CR016A Copper vs. Z40101 Zinc

CR016A copper belongs to the copper alloys classification, while Z40101 zinc belongs to the zinc alloys.

For each property being compared, the top bar is CR016A copper and the bottom bar is Z40101 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
87
Elongation at Break, % 15
44
Poisson's Ratio 0.34
0.25
Shear Modulus, GPa 43
35
Tensile Strength: Ultimate (UTS), MPa 230
130
Tensile Strength: Yield (Proof), MPa 140
110

Thermal Properties

Latent Heat of Fusion, J/g 210
110
Maximum Temperature: Mechanical, °C 200
90
Melting Completion (Liquidus), °C 1090
410
Melting Onset (Solidus), °C 1040
400
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 390
110
Thermal Expansion, µm/m-K 17
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 98
27
Electrical Conductivity: Equal Weight (Specific), % IACS 99
37

Otherwise Unclassified Properties

Base Metal Price, % relative 35
11
Density, g/cm3 9.0
6.6
Embodied Carbon, kg CO2/kg material 2.7
2.8
Embodied Energy, MJ/kg 42
53
Embodied Water, L/kg 390
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
56
Resilience: Unit (Modulus of Resilience), kJ/m3 83
69
Stiffness to Weight: Axial, points 7.2
7.4
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 7.1
5.7
Strength to Weight: Bending, points 9.3
8.9
Thermal Diffusivity, mm2/s 110
44
Thermal Shock Resistance, points 8.1
4.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Bismuth (Bi), % 0 to 0.00050
0
Cadmium (Cd), % 0
0 to 0.0050
Copper (Cu), % 99.843 to 99.919
0.080 to 0.4
Iron (Fe), % 0
0 to 0.010
Lead (Pb), % 0
0 to 0.010
Phosphorus (P), % 0.0010 to 0.0070
0
Silver (Ag), % 0.080 to 0.12
0
Tin (Sn), % 0
0 to 0.0030
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 0
99.542 to 99.92