CR019A Copper vs. AWS BCo-1

CR019A copper belongs to the copper alloys classification, while AWS BCo-1 belongs to the cobalt alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is CR019A copper and the bottom bar is AWS BCo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Poisson's Ratio 0.34
0.3
Shear Modulus, GPa 43
78
Tensile Strength: Ultimate (UTS), MPa 220
700

Thermal Properties

Latent Heat of Fusion, J/g 210
420
Melting Completion (Liquidus), °C 1090
1150
Melting Onset (Solidus), °C 1040
1120
Specific Heat Capacity, J/kg-K 390
480
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.1
Embodied Carbon, kg CO2/kg material 2.7
8.0
Embodied Energy, MJ/kg 42
110
Embodied Water, L/kg 390
430

Common Calculations

Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 6.8
24
Strength to Weight: Bending, points 9.0
22
Thermal Shock Resistance, points 7.8
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.050
Bismuth (Bi), % 0 to 0.00050
0
Boron (B), % 0
0.7 to 0.9
Carbon (C), % 0
0.35 to 0.45
Chromium (Cr), % 0
18 to 20
Cobalt (Co), % 0
46 to 54
Copper (Cu), % 99.874 to 99.92
0
Iron (Fe), % 0
0 to 1.0
Nickel (Ni), % 0
16 to 18
Phosphorus (P), % 0
0 to 0.020
Selenium (Se), % 0
0 to 0.0050
Silicon (Si), % 0
7.5 to 8.5
Silver (Ag), % 0.080 to 0.12
0
Sulfur (S), % 0
0 to 0.020
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0
3.5 to 4.5
Zirconium (Zr), % 0
0 to 0.050
Residuals, % 0
0 to 0.5