CR019A Copper vs. Class 2 Tungsten

CR019A copper belongs to the copper alloys classification, while class 2 tungsten belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR019A copper and the bottom bar is class 2 tungsten.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
260
Elongation at Break, % 15
5.7
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
100
Tensile Strength: Ultimate (UTS), MPa 220
860
Tensile Strength: Yield (Proof), MPa 130
580

Thermal Properties

Latent Heat of Fusion, J/g 210
160
Specific Heat Capacity, J/kg-K 390
120
Thermal Conductivity, W/m-K 390
20
Thermal Expansion, µm/m-K 17
4.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
13
Electrical Conductivity: Equal Weight (Specific), % IACS 100
7.8

Otherwise Unclassified Properties

Density, g/cm3 9.0
15
Embodied Carbon, kg CO2/kg material 2.7
23
Embodied Energy, MJ/kg 42
350
Embodied Water, L/kg 390
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
44
Resilience: Unit (Modulus of Resilience), kJ/m3 76
640
Stiffness to Weight: Axial, points 7.2
9.6
Stiffness to Weight: Bending, points 18
14
Strength to Weight: Axial, points 6.8
16
Strength to Weight: Bending, points 9.0
13
Thermal Diffusivity, mm2/s 110
11
Thermal Shock Resistance, points 7.8
52

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.874 to 99.92
0
Silver (Ag), % 0.080 to 0.12
0
Tungsten (W), % 0
92.5
Residuals, % 0
7.5