MakeItFrom.com
Menu (ESC)

CR019A Copper vs. C11100 Copper

Both CR019A copper and C11100 copper are copper alloys. Their average alloy composition is basically identical. There are 28 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is CR019A copper and the bottom bar is C11100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 15
1.5
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
44
Tensile Strength: Ultimate (UTS), MPa 220
460
Tensile Strength: Yield (Proof), MPa 130
420

Thermal Properties

Latent Heat of Fusion, J/g 210
210
Maximum Temperature: Mechanical, °C 200
200
Melting Completion (Liquidus), °C 1090
1080
Melting Onset (Solidus), °C 1040
1070
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 390
390
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
100
Electrical Conductivity: Equal Weight (Specific), % IACS 100
100

Otherwise Unclassified Properties

Base Metal Price, % relative 35
31
Density, g/cm3 9.0
9.0
Embodied Carbon, kg CO2/kg material 2.7
2.6
Embodied Energy, MJ/kg 42
41
Embodied Water, L/kg 390
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
6.6
Resilience: Unit (Modulus of Resilience), kJ/m3 76
750
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 6.8
14
Strength to Weight: Bending, points 9.0
15
Thermal Diffusivity, mm2/s 110
110
Thermal Shock Resistance, points 7.8
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.874 to 99.92
99.9 to 100
Silver (Ag), % 0.080 to 0.12
0
Residuals, % 0
0 to 0.1