CR019A Copper vs. R31233 Cobalt

CR019A copper belongs to the copper alloys classification, while R31233 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CR019A copper and the bottom bar is R31233 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
220
Elongation at Break, % 15
17
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
85
Tensile Strength: Ultimate (UTS), MPa 220
1020
Tensile Strength: Yield (Proof), MPa 130
420

Thermal Properties

Latent Heat of Fusion, J/g 210
320
Melting Completion (Liquidus), °C 1090
1350
Melting Onset (Solidus), °C 1040
1330
Specific Heat Capacity, J/kg-K 390
440
Thermal Conductivity, W/m-K 390
12
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 100
2.1

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.6
Embodied Carbon, kg CO2/kg material 2.7
8.4
Embodied Energy, MJ/kg 42
110
Embodied Water, L/kg 390
480

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
140
Resilience: Unit (Modulus of Resilience), kJ/m3 76
410
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 6.8
33
Strength to Weight: Bending, points 9.0
26
Thermal Diffusivity, mm2/s 110
3.2
Thermal Shock Resistance, points 7.8
25

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Boron (B), % 0
0 to 0.015
Carbon (C), % 0
0.020 to 0.1
Chromium (Cr), % 0
23.5 to 27.5
Cobalt (Co), % 0
44.7 to 63.3
Copper (Cu), % 99.874 to 99.92
0
Iron (Fe), % 0
1.0 to 5.0
Manganese (Mn), % 0
0.1 to 1.5
Molybdenum (Mo), % 0
4.0 to 6.0
Nickel (Ni), % 0
7.0 to 11
Nitrogen (N), % 0
0.030 to 0.12
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0.050 to 1.0
Silver (Ag), % 0.080 to 0.12
0
Sulfur (S), % 0
0 to 0.020
Tungsten (W), % 0
1.0 to 3.0