CR020A Copper vs. C41300 Brass

Both CR020A copper and C41300 brass are copper alloys. They have a moderately high 91% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CR020A copper and the bottom bar is C41300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Elongation at Break, % 15
2.0 to 44
Poisson's Ratio 0.34
0.33
Shear Modulus, GPa 43
42
Tensile Strength: Ultimate (UTS), MPa 220
300 to 630
Tensile Strength: Yield (Proof), MPa 130
120 to 570

Thermal Properties

Latent Heat of Fusion, J/g 210
200
Maximum Temperature: Mechanical, °C 200
180
Melting Completion (Liquidus), °C 1090
1040
Melting Onset (Solidus), °C 1040
1010
Specific Heat Capacity, J/kg-K 390
380
Thermal Conductivity, W/m-K 380
130
Thermal Expansion, µm/m-K 17
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
30
Electrical Conductivity: Equal Weight (Specific), % IACS 100
31

Otherwise Unclassified Properties

Base Metal Price, % relative 31
29
Density, g/cm3 9.0
8.7
Embodied Carbon, kg CO2/kg material 2.6
2.7
Embodied Energy, MJ/kg 41
44
Embodied Water, L/kg 320
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
11 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 76
69 to 1440
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 6.8
9.6 to 20
Strength to Weight: Bending, points 9.0
11 to 19
Thermal Diffusivity, mm2/s 110
40
Thermal Shock Resistance, points 7.8
11 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.95 to 99.999
89 to 93
Iron (Fe), % 0
0 to 0.050
Lead (Pb), % 0 to 0.0050
0 to 0.1
Phosphorus (P), % 0.0010 to 0.0060
0
Silver (Ag), % 0 to 0.015
0
Tin (Sn), % 0
0.7 to 1.3
Zinc (Zn), % 0
5.1 to 10.3
Residuals, % 0
0 to 0.5