CR020A Copper vs. C44500 Brass

Both CR020A copper and C44500 brass are copper alloys. They have 72% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CR020A copper and the bottom bar is C44500 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
110
Poisson's Ratio 0.34
0.32
Shear Modulus, GPa 43
41
Tensile Strength: Ultimate (UTS), MPa 220
350
Tensile Strength: Yield (Proof), MPa 130
120

Thermal Properties

Latent Heat of Fusion, J/g 210
180
Maximum Temperature: Mechanical, °C 200
140
Melting Completion (Liquidus), °C 1090
940
Melting Onset (Solidus), °C 1040
900
Specific Heat Capacity, J/kg-K 390
380
Thermal Conductivity, W/m-K 380
110
Thermal Expansion, µm/m-K 17
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
25
Electrical Conductivity: Equal Weight (Specific), % IACS 100
27

Otherwise Unclassified Properties

Base Metal Price, % relative 31
26
Density, g/cm3 9.0
8.3
Embodied Carbon, kg CO2/kg material 2.6
2.7
Embodied Energy, MJ/kg 41
46
Embodied Water, L/kg 320
330

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 76
65
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
19
Strength to Weight: Axial, points 6.8
12
Strength to Weight: Bending, points 9.0
13
Thermal Diffusivity, mm2/s 110
35
Thermal Shock Resistance, points 7.8
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Bismuth (Bi), % 0 to 0.00050
0
Copper (Cu), % 99.95 to 99.999
70 to 73
Iron (Fe), % 0
0 to 0.060
Lead (Pb), % 0 to 0.0050
0 to 0.070
Phosphorus (P), % 0.0010 to 0.0060
0.020 to 0.1
Silver (Ag), % 0 to 0.015
0
Tin (Sn), % 0
0.9 to 1.2
Zinc (Zn), % 0
25.2 to 29.1
Residuals, % 0
0 to 0.4