CR020A Copper vs. R30012 Cobalt

CR020A copper belongs to the copper alloys classification, while R30012 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR020A copper and the bottom bar is R30012 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
220
Elongation at Break, % 15
1.0
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
86
Tensile Strength: Ultimate (UTS), MPa 220
830
Tensile Strength: Yield (Proof), MPa 130
650

Thermal Properties

Latent Heat of Fusion, J/g 210
320
Melting Completion (Liquidus), °C 1090
1470
Melting Onset (Solidus), °C 1040
1280
Specific Heat Capacity, J/kg-K 390
440
Thermal Conductivity, W/m-K 380
15
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 100
1.8

Otherwise Unclassified Properties

Density, g/cm3 9.0
8.8
Embodied Carbon, kg CO2/kg material 2.6
8.3
Embodied Energy, MJ/kg 41
120
Embodied Water, L/kg 320
480

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 29
7.7
Resilience: Unit (Modulus of Resilience), kJ/m3 76
960
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 6.8
26
Strength to Weight: Bending, points 9.0
22
Thermal Diffusivity, mm2/s 110
3.8
Thermal Shock Resistance, points 7.8
23

Alloy Composition

Bismuth (Bi), % 0 to 0.00050
0
Carbon (C), % 0
1.4 to 2.0
Chromium (Cr), % 0
27 to 32
Cobalt (Co), % 0
47.5 to 64.1
Copper (Cu), % 99.95 to 99.999
0
Iron (Fe), % 0
0 to 3.0
Lead (Pb), % 0 to 0.0050
0
Molybdenum (Mo), % 0
0 to 1.0
Nickel (Ni), % 0
0 to 3.0
Phosphorus (P), % 0.0010 to 0.0060
0
Silicon (Si), % 0
0 to 2.0
Silver (Ag), % 0 to 0.015
0
Tungsten (W), % 0
7.5 to 9.5