CR022A Copper vs. ASTM A209 Steel

CR022A copper belongs to the copper alloys classification, while ASTM A209 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is ASTM A209 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
34
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
73
Tensile Strength: Ultimate (UTS), MPa 230
420 to 460
Tensile Strength: Yield (Proof), MPa 140
220 to 250

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
410
Melting Completion (Liquidus), °C 1090
1470
Melting Onset (Solidus), °C 1040
1420 to 1430
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
50
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.1 to 8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 31
2.4
Density, g/cm3 9.0
7.9
Embodied Carbon, kg CO2/kg material 2.6
1.5
Embodied Energy, MJ/kg 41
20
Embodied Water, L/kg 310
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 83
130 to 170
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
15 to 16
Strength to Weight: Bending, points 9.3
16 to 17
Thermal Diffusivity, mm2/s 110
13
Thermal Shock Resistance, points 8.1
12 to 14