CR022A Copper vs. EN 1.0553 Steel

CR022A copper belongs to the copper alloys classification, while EN 1.0553 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is EN 1.0553 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
190
Elongation at Break, % 15
20
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
73
Tensile Strength: Ultimate (UTS), MPa 230
530
Tensile Strength: Yield (Proof), MPa 140
330

Thermal Properties

Latent Heat of Fusion, J/g 210
250
Maximum Temperature: Mechanical, °C 200
400
Melting Completion (Liquidus), °C 1090
1460
Melting Onset (Solidus), °C 1040
1420
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 380
51
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 100
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.9
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 41
19
Embodied Water, L/kg 310
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
93
Resilience: Unit (Modulus of Resilience), kJ/m3 83
290
Stiffness to Weight: Axial, points 7.2
13
Stiffness to Weight: Bending, points 18
24
Strength to Weight: Axial, points 7.1
19
Strength to Weight: Bending, points 9.3
18
Thermal Diffusivity, mm2/s 110
14
Thermal Shock Resistance, points 8.1
17

Alloy Composition

Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Carbon (C), % 0
0 to 0.24
Copper (Cu), % 99.99 to 99.999
0 to 0.6
Iron (Fe), % 0 to 0.0010
96.8 to 100
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0 to 1.7
Nickel (Ni), % 0 to 0.0010
0
Nitrogen (N), % 0
0 to 0.014
Phosphorus (P), % 0.0010 to 0.0060
0 to 0.040
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.6
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.040
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Zinc (Zn), % 0 to 0.00010
0