CR022A Copper vs. EN 1.4309 Stainless Steel

CR022A copper belongs to the copper alloys classification, while EN 1.4309 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is EN 1.4309 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 15
34
Poisson's Ratio 0.34
0.28
Shear Modulus, GPa 43
77
Tensile Strength: Ultimate (UTS), MPa 230
490
Tensile Strength: Yield (Proof), MPa 140
210

Thermal Properties

Latent Heat of Fusion, J/g 210
290
Maximum Temperature: Mechanical, °C 200
960
Melting Completion (Liquidus), °C 1090
1420
Melting Onset (Solidus), °C 1040
1380
Specific Heat Capacity, J/kg-K 390
480
Thermal Conductivity, W/m-K 380
15
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 100
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 31
16
Density, g/cm3 9.0
7.8
Embodied Carbon, kg CO2/kg material 2.6
3.1
Embodied Energy, MJ/kg 41
45
Embodied Water, L/kg 310
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
140
Resilience: Unit (Modulus of Resilience), kJ/m3 83
110
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
25
Strength to Weight: Axial, points 7.1
18
Strength to Weight: Bending, points 9.3
18
Thermal Diffusivity, mm2/s 110
4.1
Thermal Shock Resistance, points 8.1
11

Alloy Composition

Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
18 to 20
Copper (Cu), % 99.99 to 99.999
0
Iron (Fe), % 0 to 0.0010
64.2 to 73
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0 to 2.0
Nickel (Ni), % 0 to 0.0010
9.0 to 12
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0.0010 to 0.0060
0 to 0.035
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 1.5
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.025
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Zinc (Zn), % 0 to 0.00010
0