CR022A Copper vs. EN 2.4663 Nickel

CR022A copper belongs to the copper alloys classification, while EN 2.4663 nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is EN 2.4663 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
210
Elongation at Break, % 15
40
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 43
81
Tensile Strength: Ultimate (UTS), MPa 230
780
Tensile Strength: Yield (Proof), MPa 140
310

Thermal Properties

Latent Heat of Fusion, J/g 210
320
Maximum Temperature: Mechanical, °C 200
1010
Melting Completion (Liquidus), °C 1090
1430
Melting Onset (Solidus), °C 1040
1380
Specific Heat Capacity, J/kg-K 390
450
Thermal Conductivity, W/m-K 380
13
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 100
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
75
Density, g/cm3 9.0
8.6
Embodied Carbon, kg CO2/kg material 2.6
11
Embodied Energy, MJ/kg 41
140
Embodied Water, L/kg 310
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
250
Resilience: Unit (Modulus of Resilience), kJ/m3 83
230
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 18
23
Strength to Weight: Axial, points 7.1
25
Strength to Weight: Bending, points 9.3
22
Thermal Diffusivity, mm2/s 110
3.5
Thermal Shock Resistance, points 8.1
22

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.4
Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Boron (B), % 0
0 to 0.0060
Cadmium (Cd), % 0 to 0.00010
0
Carbon (C), % 0
0.050 to 0.1
Chromium (Cr), % 0
20 to 23
Cobalt (Co), % 0
11 to 14
Copper (Cu), % 99.99 to 99.999
0 to 0.5
Iron (Fe), % 0 to 0.0010
0 to 2.0
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0 to 0.2
Molybdenum (Mo), % 0
8.5 to 10
Nickel (Ni), % 0 to 0.0010
48 to 59.6
Phosphorus (P), % 0.0010 to 0.0060
0 to 0.010
Selenium (Se), % 0 to 0.00020
0
Silicon (Si), % 0
0 to 0.2
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0 to 0.010
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Titanium (Ti), % 0
0.2 to 0.6
Zinc (Zn), % 0 to 0.00010
0