CR022A Copper vs. C12000 Copper

Both CR022A copper and C12000 copper are copper alloys. Their average alloy composition is basically identical. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is CR022A copper and the bottom bar is C12000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
120
Elongation at Break, % 15
2.8 to 50
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 43
43
Tensile Strength: Ultimate (UTS), MPa 230
230 to 410
Tensile Strength: Yield (Proof), MPa 140
77 to 400

Thermal Properties

Latent Heat of Fusion, J/g 210
210
Maximum Temperature: Mechanical, °C 200
200
Melting Completion (Liquidus), °C 1090
1080
Melting Onset (Solidus), °C 1040
1080
Specific Heat Capacity, J/kg-K 390
390
Thermal Conductivity, W/m-K 380
390
Thermal Expansion, µm/m-K 17
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 100
98
Electrical Conductivity: Equal Weight (Specific), % IACS 100
98

Otherwise Unclassified Properties

Base Metal Price, % relative 31
31
Density, g/cm3 9.0
9.0
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 41
41
Embodied Water, L/kg 310
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31
10 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 83
25 to 690
Stiffness to Weight: Axial, points 7.2
7.2
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 7.1
7.2 to 13
Strength to Weight: Bending, points 9.3
9.4 to 14
Thermal Diffusivity, mm2/s 110
110
Thermal Shock Resistance, points 8.1
8.2 to 15

Alloy Composition

Antimony (Sb), % 0 to 0.00040
0
Arsenic (As), % 0 to 0.00050
0
Bismuth (Bi), % 0 to 0.00020
0
Cadmium (Cd), % 0 to 0.00010
0
Copper (Cu), % 99.99 to 99.999
99.9 to 99.996
Iron (Fe), % 0 to 0.0010
0
Lead (Pb), % 0 to 0.00050
0
Manganese (Mn), % 0 to 0.00050
0
Nickel (Ni), % 0 to 0.0010
0
Phosphorus (P), % 0.0010 to 0.0060
0.0040 to 0.012
Selenium (Se), % 0 to 0.00020
0
Silver (Ag), % 0 to 0.0025
0
Sulfur (S), % 0 to 0.0015
0
Tellurium (Te), % 0 to 0.00020
0
Tin (Sn), % 0 to 0.00020
0
Zinc (Zn), % 0 to 0.00010
0