EN-MC21120 Magnesium vs. 6110 Aluminum

EN-MC21120 magnesium belongs to the magnesium alloys classification, while 6110 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN-MC21120 magnesium and the bottom bar is 6110 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 46
70
Elongation at Break, % 2.2 to 6.7
2.2
Fatigue Strength, MPa 84 to 96
120
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 18
26
Shear Strength, MPa 110 to 160
290
Tensile Strength: Ultimate (UTS), MPa 200 to 270
500
Tensile Strength: Yield (Proof), MPa 130 to 170
500

Thermal Properties

Latent Heat of Fusion, J/g 350
410
Maximum Temperature: Mechanical, °C 130
170
Melting Completion (Liquidus), °C 600
640
Melting Onset (Solidus), °C 490
600
Specific Heat Capacity, J/kg-K 990
900
Thermal Conductivity, W/m-K 76
170
Thermal Expansion, µm/m-K 26
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
42
Electrical Conductivity: Equal Weight (Specific), % IACS 59
140

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.5
Density, g/cm3 1.7
2.8
Embodied Carbon, kg CO2/kg material 22
8.2
Embodied Energy, MJ/kg 160
150
Embodied Water, L/kg 990
1170

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 5.0 to 15
11
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 320
1770
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
50
Strength to Weight: Axial, points 31 to 43
51
Strength to Weight: Bending, points 43 to 53
51
Thermal Diffusivity, mm2/s 44
67
Thermal Shock Resistance, points 11 to 16
22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 8.3 to 9.7
94.4 to 98.4
Chromium (Cr), % 0
0.040 to 0.25
Copper (Cu), % 0 to 0.030
0.2 to 0.7
Iron (Fe), % 0 to 0.0050
0 to 0.8
Magnesium (Mg), % 88.6 to 91.3
0.5 to 1.1
Manganese (Mn), % 0.1 to 0.5
0.2 to 0.7
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0 to 0.2
0.7 to 1.5
Titanium (Ti), % 0
0 to 0.15
Zinc (Zn), % 0.35 to 1.0
0 to 0.3
Residuals, % 0 to 0.010
0 to 0.15