MakeItFrom.com
Menu (ESC)

EN-MC21210 Magnesium vs. 332.0 Aluminum

EN-MC21210 magnesium belongs to the magnesium alloys classification, while 332.0 aluminum belongs to the aluminum alloys.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is 332.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
110
Elastic (Young's, Tensile) Modulus, GPa 44
73
Elongation at Break, % 14
1.0
Fatigue Strength, MPa 70
90
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 17
27
Shear Strength, MPa 110
190
Tensile Strength: Ultimate (UTS), MPa 190
250
Tensile Strength: Yield (Proof), MPa 90
190

Thermal Properties

Latent Heat of Fusion, J/g 350
530
Maximum Temperature: Mechanical, °C 100
170
Melting Completion (Liquidus), °C 600
580
Melting Onset (Solidus), °C 570
530
Specific Heat Capacity, J/kg-K 1000
880
Thermal Conductivity, W/m-K 120
100
Thermal Expansion, µm/m-K 27
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
26
Electrical Conductivity: Equal Weight (Specific), % IACS 130
84

Otherwise Unclassified Properties

Base Metal Price, % relative 12
10
Density, g/cm3 1.6
2.8
Embodied Carbon, kg CO2/kg material 24
7.8
Embodied Energy, MJ/kg 160
140
Embodied Water, L/kg 980
1040

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
2.3
Resilience: Unit (Modulus of Resilience), kJ/m3 92
250
Stiffness to Weight: Axial, points 15
15
Stiffness to Weight: Bending, points 72
50
Strength to Weight: Axial, points 32
24
Strength to Weight: Bending, points 44
31
Thermal Diffusivity, mm2/s 76
42
Thermal Shock Resistance, points 11
12

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
80.1 to 89
Copper (Cu), % 0 to 0.010
2.0 to 4.0
Iron (Fe), % 0 to 0.0050
0 to 1.2
Magnesium (Mg), % 96.3 to 98.3
0.5 to 1.5
Manganese (Mn), % 0.1 to 0.7
0 to 0.5
Nickel (Ni), % 0 to 0.0020
0 to 0.5
Silicon (Si), % 0 to 0.1
8.5 to 10.5
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0 to 0.2
0 to 1.0
Residuals, % 0 to 0.010
0 to 0.5