EN-MC21210 Magnesium vs. AISI 303Se Stainless Steel

EN-MC21210 magnesium belongs to the magnesium alloys classification, while AISI 303Se stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is AISI 303Se stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
180
Elastic (Young's, Tensile) Modulus, GPa 44
200
Elongation at Break, % 14
45
Fatigue Strength, MPa 70
210
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
77
Shear Strength, MPa 110
410
Tensile Strength: Ultimate (UTS), MPa 190
590
Tensile Strength: Yield (Proof), MPa 90
230

Thermal Properties

Latent Heat of Fusion, J/g 350
290
Maximum Temperature: Mechanical, °C 100
930
Melting Completion (Liquidus), °C 600
1420
Melting Onset (Solidus), °C 570
1380
Specific Heat Capacity, J/kg-K 1000
480
Thermal Conductivity, W/m-K 120
16
Thermal Expansion, µm/m-K 27
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 130
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 12
16
Density, g/cm3 1.6
7.8
Embodied Carbon, kg CO2/kg material 24
3.0
Embodied Energy, MJ/kg 160
42
Embodied Water, L/kg 980
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
210
Resilience: Unit (Modulus of Resilience), kJ/m3 92
130
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 72
25
Strength to Weight: Axial, points 32
21
Strength to Weight: Bending, points 44
20
Thermal Diffusivity, mm2/s 76
4.3
Thermal Shock Resistance, points 11
13

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
67.2 to 74.9
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0 to 2.0
Nickel (Ni), % 0 to 0.0020
8.0 to 10
Phosphorus (P), % 0
0 to 0.2
Selenium (Se), % 0
0.15 to 0.35
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.060
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0