EN-MC21210 Magnesium vs. ASTM A387 Grade 91 Class 2

EN-MC21210 magnesium belongs to the magnesium alloys classification, while ASTM A387 grade 91 class 2 belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is ASTM A387 grade 91 class 2.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
200
Elastic (Young's, Tensile) Modulus, GPa 44
190
Elongation at Break, % 14
20
Fatigue Strength, MPa 70
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
75
Shear Strength, MPa 110
420
Tensile Strength: Ultimate (UTS), MPa 190
670
Tensile Strength: Yield (Proof), MPa 90
470

Thermal Properties

Latent Heat of Fusion, J/g 350
270
Maximum Temperature: Mechanical, °C 100
600
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 570
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 120
26
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 130
10

Otherwise Unclassified Properties

Base Metal Price, % relative 12
7.0
Density, g/cm3 1.6
7.8
Embodied Carbon, kg CO2/kg material 24
2.6
Embodied Energy, MJ/kg 160
37
Embodied Water, L/kg 980
88

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
120
Resilience: Unit (Modulus of Resilience), kJ/m3 92
580
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 72
25
Strength to Weight: Axial, points 32
24
Strength to Weight: Bending, points 44
22
Thermal Diffusivity, mm2/s 76
6.9
Thermal Shock Resistance, points 11
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0 to 0.020
Carbon (C), % 0
0.080 to 0.12
Chromium (Cr), % 0
8.0 to 9.5
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
87.3 to 90.3
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0.3 to 0.6
Molybdenum (Mo), % 0
0.85 to 1.1
Nickel (Ni), % 0 to 0.0020
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0 to 0.1
0.2 to 0.5
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zinc (Zn), % 0 to 0.2
0
Zirconium (Zr), % 0
0 to 0.010
Residuals, % 0 to 0.010
0