EN-MC21210 Magnesium vs. ASTM Grade LC1 Steel

EN-MC21210 magnesium belongs to the magnesium alloys classification, while ASTM grade LC1 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is ASTM grade LC1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
160
Elastic (Young's, Tensile) Modulus, GPa 44
190
Elongation at Break, % 14
27
Fatigue Strength, MPa 70
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Tensile Strength: Ultimate (UTS), MPa 190
540
Tensile Strength: Yield (Proof), MPa 90
270

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 100
410
Melting Completion (Liquidus), °C 600
1470
Melting Onset (Solidus), °C 570
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 120
50
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 130
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.4
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 24
1.5
Embodied Energy, MJ/kg 160
20
Embodied Water, L/kg 980
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
120
Resilience: Unit (Modulus of Resilience), kJ/m3 92
200
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 72
24
Strength to Weight: Axial, points 32
19
Strength to Weight: Bending, points 44
19
Thermal Diffusivity, mm2/s 76
13
Thermal Shock Resistance, points 11
16

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Carbon (C), % 0
0 to 0.25
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
97.6 to 99.05
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0.5 to 0.8
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0 to 0.6
Sulfur (S), % 0
0 to 0.045
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0