EN-MC21210 Magnesium vs. EN 1.3551 Steel

EN-MC21210 magnesium belongs to the magnesium alloys classification, while EN 1.3551 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is EN 1.3551 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
220
Elastic (Young's, Tensile) Modulus, GPa 44
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
75
Tensile Strength: Ultimate (UTS), MPa 190
720

Thermal Properties

Latent Heat of Fusion, J/g 350
260
Maximum Temperature: Mechanical, °C 100
530
Melting Completion (Liquidus), °C 600
1490
Melting Onset (Solidus), °C 570
1450
Specific Heat Capacity, J/kg-K 1000
460
Thermal Conductivity, W/m-K 120
36
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
8.6
Electrical Conductivity: Equal Weight (Specific), % IACS 130
9.9

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.0
Density, g/cm3 1.6
7.9
Embodied Carbon, kg CO2/kg material 24
4.9
Embodied Energy, MJ/kg 160
71
Embodied Water, L/kg 980
82

Common Calculations

Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 72
24
Strength to Weight: Axial, points 32
26
Strength to Weight: Bending, points 44
23
Thermal Diffusivity, mm2/s 76
9.8
Thermal Shock Resistance, points 11
21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Carbon (C), % 0
0.77 to 0.85
Chromium (Cr), % 0
3.9 to 4.3
Copper (Cu), % 0 to 0.010
0 to 0.3
Iron (Fe), % 0 to 0.0050
88.8 to 91.1
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0.15 to 0.35
Molybdenum (Mo), % 0
4.0 to 4.5
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.1
0 to 0.4
Sulfur (S), % 0
0 to 0.015
Tungsten (W), % 0
0 to 0.25
Vanadium (V), % 0
0.9 to 1.1
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0