EN-MC21210 Magnesium vs. EN 1.4537 Stainless Steel

EN-MC21210 magnesium belongs to the magnesium alloys classification, while EN 1.4537 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN-MC21210 magnesium and the bottom bar is EN 1.4537 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 48
220
Elastic (Young's, Tensile) Modulus, GPa 44
210
Elongation at Break, % 14
42
Fatigue Strength, MPa 70
290
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
80
Shear Strength, MPa 110
480
Tensile Strength: Ultimate (UTS), MPa 190
700
Tensile Strength: Yield (Proof), MPa 90
330

Thermal Properties

Latent Heat of Fusion, J/g 350
310
Maximum Temperature: Mechanical, °C 100
1100
Melting Completion (Liquidus), °C 600
1440
Melting Onset (Solidus), °C 570
1390
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 120
14
Thermal Expansion, µm/m-K 27
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 130
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
34
Density, g/cm3 1.6
8.1
Embodied Carbon, kg CO2/kg material 24
6.1
Embodied Energy, MJ/kg 160
84
Embodied Water, L/kg 980
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 22
240
Resilience: Unit (Modulus of Resilience), kJ/m3 92
270
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 72
24
Strength to Weight: Axial, points 32
24
Strength to Weight: Bending, points 44
22
Thermal Diffusivity, mm2/s 76
3.7
Thermal Shock Resistance, points 11
15

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 1.6 to 2.6
0
Carbon (C), % 0
0 to 0.020
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 0 to 0.010
1.0 to 2.0
Iron (Fe), % 0 to 0.0050
36.3 to 46.1
Magnesium (Mg), % 96.3 to 98.3
0
Manganese (Mn), % 0.1 to 0.7
0 to 2.0
Molybdenum (Mo), % 0
4.7 to 5.7
Nickel (Ni), % 0 to 0.0020
24 to 27
Nitrogen (N), % 0
0.17 to 0.25
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 0.7
Sulfur (S), % 0
0 to 0.010
Zinc (Zn), % 0 to 0.2
0
Residuals, % 0 to 0.010
0